The use of stainless steel pipes is now more and more extensive. Because of its good corrosion resistance, it plays a crucial role in engineering construction. In the process of production, we need to perform solution treatment on stainless steel pipes. The main purpose is to obtain certain Martensite increases the hardness of the product. Let's take a look at the solution treatment of stainless steel pipes:
(1) The intermediate aging method is heated to (760±15) degree after the solution treatment, and the temperature is kept for 90 minutes because Cr23C6 carbides are precipitated from the austenite, which reduces the carbon and alloying elements content in the austenitic 904L stainless steel pipe , the Ms point is raised to 70 degree and then cooled to room temperature to obtain martensite plus ferrite plus retained austenite structure, and the retained austenite is decomposed after aging at 510 degree .
(2) После регулировки высокой температуры и криогенной обработки раствор сначала нагревают до 950 градусов в течение 90 минут. За счет повышения точки Ms небольшое количество мартенсита можно получить при охлаждении до комнатной температуры; количество мартенсита.
(3) После обработки на раствор методом холодной деформации проводят холодную деформацию при комнатной температуре. Количество мартенсита, образовавшегося в бесшовной трубе 904L во время холодной деформации, связано с величиной деформации и составом трубы из нержавеющей стали 904L.
Вышеупомянутые три метода обычно используются для обработки раствором труб из нержавеющей стали. Я надеюсь, что они могут помочь вам.